HSFT、HSMT是(shi)由(you)聚(ju)烯烴和熱熔膠復合生(sheng)產而成的熱收縮套管,用于保護連(lian)接、防水(shui)防腐蝕,可以在(zai)粗糙的環境中(zhong)加強固定和防震(zhen)動,具有很好(hao)的絕緣保護電(dian)子連(lian)接器的功(gong)能。與常(chang)規的連(lian)接器相比,具有耐久性、易(yi)于安裝、安裝成本低的優(you)勢(shi)。
特性
收縮率3:1
材料優(you)異的延伸(shen)性能,抗機械損害
透明度佳,提高(gao)更(geng)好的抗拉力(li)
高彈性能(neng),管材不易變形
操作溫度范圍
操作溫度: -55℃~125℃
開始收(shou)縮溫度: 80℃
最低完全收縮(suo)溫度(du): 130℃
性能參數
Test Item | Characteristics | Test condition | |
Unaged | Tensile strength | Min. 16MPa | Room temp. |
Elongation | Min. 200% | ||
Aged | Tensile strength | Min. 11.5MPa | 136℃/7 days |
Elongation | Min. 100% | ||
Voltage withstand and breakdown Voltage(Unaged) | Withstand 2.5 KV for 1minute and breakdown | Room temp. | |
Voltage withstand and breakdown Voltage(Aged) | Withstand 2.5 KV for 1minute and breakdown at least half of unaged breakdown voltage | 136℃/7 days | |
Copper corrosion | No corrosion of bare copper | 136℃/7 days | |
Copper stability | No sign of degradation Min.Elongation 100% | 136℃/7 days | |
Cold bend | No crack | -30℃/4 hrs | |
Maximum secant modulus(2%) | 250 MPa | - | |
Volume resistivity | Min.1014Ω-cm | - | |
Heat shock | No crack | 200℃/4 hrs |
產品規格-HSFT
Part. No |
Wire Range |
Tab Size(mm) | (mm) | Length(mm) | Insulator | Color | |||
A.W.G | mm2 | Size | d1 | D | W | L | |||
MDD 1-250 | 22-18 | 0.5-1.0 | 6.3 x 0.8 | 1.8 | 4.7 | 6.3 | 31 | PE | Red |
MDD 2-250 | 16-14 | 1.5-2.5 | 6.3 x 0.8 | 2.3 | 5.7 | 6.3 | 31 | PE | Blue |
MDD 5-250 | 12-10 | 4-6 | 6.3 x 0.8 | 3.5 | 6.7 | 6.3 | 33 | PE | Yellow |
產品規格-HSMT
Part. No |
Wire Range |
Tab Size(mm) | (mm) | Length(mm) | Insulator | Color | |||
A.W.G | mm2 | Size | d | D | W | L | |||
FDFD 1-250 | 22-18 | 0.5-1.0 | 6.6x 0.35 | 1.8 | 7.0 | 6.6 | 29 | PE | Red |
FDFD 2-250 | 16-14 | 1.5-2.5 | 6.6x 0.35 | 2.3 | 7.0 | 6.6 | 30 | PE | Blue |
FDFD 5-250 | 12-10 | 4.0-6.0 | 6.6x 0.35 | 3.5 | 7.0 | 6.6 | 32 | PE | Yellow |